Publication:
The impact of Er:YAG laser enamel conditioning on the microleakage of a new hydrophilic sealant-UltraSeal XT (R) hydro (TM)

Loading...
Thumbnail Image
Date
2016-05-01
Authors
GÜÇLÜ, ZEYNEP ASLI
DÖNMEZ, NAZMİYE
TÜZÜNER, TAMER
ODABAŞ, MESUT ENES
HURT, Andrew p
COLEMAN, Nicola
Journal Title
Journal ISSN
Volume Title
Publisher
Research Projects
Organizational Units
Journal Issue

Metrics

Search on Google Scholar

Abstract
UltraSeal XT hydro is a new hydrophilic, light-cured, methacrylate-based pit and fissure sealant which has been developed by Ultradent Products, USA. The sealant is highly filled with a 53 wt.% mixture of inorganic particles which confer both thixotropy and radiopacity. The principal purpose of this study was to investigate the microleakage of UltraSeal XT hydro as a function of different enamel etching techniques. The occlusal surfaces of sound, extracted human molars were either acid etched, Er:YAG laser irradiated or successively laser irradiated and acid etched. UltraSeal XT hydro was applied to each group of teeth (n = 10) which were subjected to a thermocycling process consisting of 2500 cycles between 5 and 50 °C with a dwell time of 30 s. Microleakage assessments were then carried out using 0.5% fuchsin dye and optical microscopy. The microleakage score data were analysed using the Kruskal-Wallis, Mann-Whitney U test with Bonferroni adjustment. No significant differences in microleakage were noted between the individually acid etched and laser-irradiated groups (p > 0.05); however, teeth treated with a combination of laser irradiation and acid etching demonstrated significantly lower microleakage scores (p < 0.001). Electron microscopy with energy-dispersive X-ray analysis revealed that the mineral filler component of UltraSeal XT hydro essentially comprises micrometre-sized particles of inorganic silicon-, aluminium- and barium-bearing phases. Laser etching increases the roughness of the enamel surface which causes a concentrated zoning of the filler particles at the enamel-sealant interface.
Description
Keywords
Citation
GÜÇLÜ Z. A. , DÖNMEZ N., TÜZÜNER T., ODABAŞ M. E. , HURT A. p. , COLEMAN N., -The impact of Er:YAG laser enamel conditioning on the microleakage of a new hydrophilic sealant-UltraSeal XT (R) hydro (TM)-, LASERS IN MEDICAL SCIENCE, cilt.31, ss.705-711, 2016