Publication: Synthesis and Characterization of Dendrimer-Encapsulated Iron and Iron-Oxide Nanoparticles
No Thumbnail Available
Date
2012-07-01T00:00:00Z
Authors
Authors
Baykal, A.
Toprak, M. S.
Durmus, ZEHRA
Senel, M.
SOZERI, H.
Demir, A.
Journal Title
Journal ISSN
Volume Title
Publisher
Metrics
Abstract
In this paper, a series of iron (Fe) containing nanoparticles were prepared by employing PAMAM (Poly(amidoamine), dendrimers with different generations (G0-G3) as templates and sodium borohydride as a reducing agent. The products have been characterized by TEM, FT-IR, XRD, VSM, TGA, and XPS. XRD analysis reveal low crystallinity of formed particles within the dendrimers, however, crystallinity of the nanoparticles was observed to increase with increasing generation of dendrimers. Dominant phases were determined as magnetite (Fe3O4 or maghemite, gamma-Fe2O3). XPS analysis revealed the chemical composition of nanoparticles as iron oxide which indicated the oxidation of Fe species subsequent to the reduction process, in agreement with XRD analysis. The magnetization curves have superparamagnetic nonhysteretic characteristic at lower fields and with nonsaturation characteristic at high fields. Magnetic evaluation of samples with the 20:1 molar ratio of Fe:PAMAM showed decreasing superparamagnetic character and decreasing saturation magnetisation with increasing generation of dendrimers.
Description
Keywords
Citation
Baykal A., Toprak M. S. , Durmus Z., Senel M., SOZERI H., Demir A., -Synthesis and Characterization of Dendrimer-Encapsulated Iron and Iron-Oxide Nanoparticles-, JOURNAL OF SUPERCONDUCTIVITY AND NOVEL MAGNETISM, cilt.25, ss.1541-1549, 2012