Farklı estetik abutmentların döngüsel yorulma yüklemesi sonrasında kırılma dayanımlarının değerlendirilmesi / The evaluation of the ftacture strenght of different esthetic abutment after cyclic fatique loading
Abstract
The aim of this study was to compare the fracture strength of peek abutments and zirconium abutments which are widely preferred instead of titanium abutments in the esthetic zone for the implant supported fixed prosthesis. In this study, the fracture strength of zirconium and peek abutments were compared after aging by chewing simulator. Study groups were; Group 1: 10 zirconium abutments on the implants (Bredent, Germany, 12 mm length and 4 mm diameter) , Group 2: Peek abutments on the implants (Bredent, Germany, 12 mm length and 4 mm diameter). All implants are embeded into an acrylic resin (Paladent-Kulzer) with 45° angle and torqued with 25 N to the implants. Afterwards, zirconia cores (Zenostar T2 Wieland) were cemented with temporary implant cement (Premier; ABD). Fatique test was performed with a chewing simulator for 1,2 million cycles. Subsequently, load to fracture test was applied by a loading device (Shimadzu, Japan) to all specimens with a speed of 1mm/ min. The fracture strength values were 478,83± 66,72 N for peek abutment group and 722,50± 84,71 N for zirconium abutment group. The results were statistically analysed with T-test. The fracture strength of zirconia abutments were statistically significantly higher than peek abutments (p< 0,001). Key words: Zirconia, ceramic, peek, abutment, fracture strength {{abstract}}
Subject
Collections
Related items
Showing items related by title, author, creator and subject.
-
Farklı bonding adezivlerinin termal siklus sonrası su absorpsiyon miktarına bağlı olarak lazer uygulamasında yapısal madde kayıplarının incelenmesi / Evaluation of structural loss caused by laser application on different bonding adhesives in relation to the quantity of absorbed water following thermal cyclus procedure
Temuçin, Fatih (Bezmialem Vakıf University, 2017)In today's dentistry, patients who undergo orthodontic treatment prefer ceramic brackets instead of metal brackets, due to their aesthetic appearance. One of the major disadvantages of the ceramic brackets is the difficulty ... -
Braket Altında Oluşan Mikrosızıntının Dört Farklı Bonding TekniğindeTermal Siklus ve Çiğneme Similatörü Yöntemleri ile Karşılaştırmalı Olarak Değerlendirilmesi
Ok, Ufuk (Bezmialem Vakıf University, 2017)The microleakage caused by the shrinkage of the adhesive related to the polymerization reaction causes weakening of the connection between the bracket and the tooth surface and leads to the penetration of bacteria. Increased ... -
Farklı adezivlerin kullanıldığı ortodontik bonding sonrası açığa çıkan BİS-GMA'nın in-vivo şartlarda değerlendirilmesi / Evaluation of BİS-GMA following orthodontic bonding with different adhesives: An in vivo study
Görükmez, Erhan (Bezmialem Vakıf University, 2017)In composite adhesives used in orthodontic clinics, ease of use, good adhesion to the enamel surface and resistance to occlusal forces are the main criteria of choice. However, besides these factors, the biocompatibility ...