Temperature Changes of Pulp Chamber during In Vitro Laser Welding of Orthodontic Attachments

Loading...
Thumbnail Image

Date

2014-01-01T00:00:00Z

Authors

Authors

Isman, Eren
Oksayan, Ridvan
Sokucu, Oral
Usumez, Serdar

Journal Title

Journal ISSN

Volume Title

Publisher

Research Projects

Organizational Units

Journal Issue

Metrics

Search on Google Scholar

Abstract

The use of lasers has been suggested for orthodontists to fabricate or repair orthodontic appliances by welding metals directly in the mouth. This work aimed to evaluate the temperature changes in the pulp chamber during welding of an orthodontic wire to an orthodontic molar band using Nd : YAG laser in vitro. A freshly extracted human third molar with eliminated pulpal tissues was used. J-type thermocouple wire was positioned in the pulp chamber. A conductor gel was used in the transferring of outside temperature changes to the thermocouple wire. An orthodontic band was applied to the molar tooth and bonded using light cured orthodontic cement. Twenty five mm length of 0.6 mm diameter orthodontic stainless steel wires was welded to the orthodontic band using Nd : YAG laser operated at 9.4 watt. Temperature variation was determined as the change from baseline temperature to the highest temperature was recorded during welding. The recorded temperature changes were between 1.8 and 6.8 degrees C (mean: 3.3 +/- 1.1 degrees C). The reported critical 5.5 degrees C level was exceeded in only one sample. The results of this study suggest that intraoral use of lasers holds great potential for the future of orthodontics and does not present a thermal risk. Further studies with larger samples and structural analysis are required.

Description

Keywords

dental materials

Citation

Page Views

0

File Downloads

51

Sustainable Development Goals