Effect of polymerization time and home bleaching agent on the microhardness and surface roughness of bulk-fill composites: A scanning electron microscopy study

Abstract

Objective: The aim of this study is to evaluate the microhardness and surface roughness of two different bulk-fill composites polymerized with light-curing unit (LCU) with different polymerization times before and after the application of a home bleaching agent.

Materials-methods: For both microhardness and surface roughness tests, 6 groups were prepared with bulk-fill materials (SonicFill, Filtek Bulk Fill) according to different polymerization times (10, 20, and 30 s). 102 specimens were prepared using Teflon molds (4 mm depth and 5 mm diameter) and polymerized with LCU. 30 specimens (n = 5) were assessed for microhardness. Before home bleaching agent application, the bottom/top (B/T) microhardness ratio was evaluated. After bleaching agent application, the microhardness measurements were performed on top surfaces. Roughness measurements were performed in 72 specimens (n = 12) before and after bleaching application. Additionally, for SEM analyses, two specimens from all tested groups were prepared before and after bleaching agent application. The data B/T microhardness ratio before bleaching was analyzed by two-way ANOVA and Tukey's HSD test. The data from the top surface of specimens' microhardness before and after bleaching were analyzed using Wilcoxon signed-rank test, Kruskal-Wallis, Mann-Whitney U tests. The data from surface roughness tests were statistically analyzed by multivariate analysis of variance and Bonferroni test (p < 0.05).

Results: The B/T microhardness ratio results revealed no significant differences between groups (p > 0.05). Comparing the microhardness values of the composites' top surfaces before and after bleaching, a significant decrease was observed exclusively in FB30s (p < 0.05). No significant differences in surface roughness values were observed when the groups were compared based on bulk-fill materials (p > 0.05) while the polymerization time affected the surface roughness of the SF20s and SF30s groups (p < 0.05). After bleaching, surface roughness values were significantly increased in the SF20s and SF30s groups (p < 0.05).

Conclusion: The clinicians should adhere to the polymerization time recommended by the manufacturer to ensure the durability of the composite material in the oral environment.