Color Change of Different Dual-Cure Resin Cements After Thermocycling

Abstract

The purpose of this study is to evaluate the effect of thermocycling on the color change of the amine-free dual-cure resin cements. IPS e. max CAD blocs were cut into specimens of 1 mm thickness (N=28) and cemented with one of the 4 different amine-free dual-cure resin cements (NX3 Nexus [NX], Kerr Dental; Variolink Esthetic DC [VE], Ivoclar Vivadent; Panavia V5 [PV], Kuraray Dental; G-CEM Linkforce [GC], GC Corporation) (n=7). A spectrophotometer was used for color measurements. Specimens were subjected to thermocycling (5 degrees C and 55 degrees C; 5000 and 10000 cycles). Normality of data distribution was tested by using the Kolmogorov-Smirnov test. Statistical analysis was performed using a two-way analysis of variance (ANOVA) and Tukey-s multiple comparison tests at a significance level of p0.05). There were no statistically significant differences between the Delta E0 and Delta E1 values of the GC group, however the other groups were affected after 10000 thermocycling (p>0.05). Amine-free resin cements used for cementation showed color change after thermocycling except GC group. All resin cements were showed clinically acceptable color change after thermocycling (Delta E<3.5).