Atomic force microscopy investigation of lithium disilicate glass ceramic after various surface treatments

No Thumbnail Available
Date
2014-07-01T00:00:00Z
Authors
Kara, H. B.
Kara, O.
Sayin, G.
Cakan, U.
Ozturk, A. N.
Journal Title
Journal ISSN
Volume Title
Publisher
Research Projects
Sustainable Development Goals
Organizational Units
Journal Issue
Abstract
The aim of this study is to evaluate the influence of various surface treatments on the surface roughness of a lithium disilicate glass ceramic. A total of 25 discs of lithium disilicate glass ceramic were prepared. Specimens were divided into five groups: (1) no treatment, (2) air abrasion, (3) acid etching, (4) Nd:YAG laser irradiation and (5) Er:YAG laser irradiation. Digital images from the surfaces were obtained by means of an atomic force microscope in tapping mode. Surface roughness was measured in 10x10 mu m boxes. Surface roughness data were analysed by one way analysis of variance. The air abrasion group (550 +/- 212 nm) had a significantly higher mean surface roughness value than the other groups. The acid etching group (392 +/- 157 nm) had a significantly higher mean roughness value than the control group (228 +/- 105 nm). Surface roughness of lithium disilicate glass ceramic was not increased by any of the laser irradiation treatments.
Description
Keywords
Citation
Kara H. B. , Kara O., Sayin G., Cakan U., Ozturk A. N. , -Atomic force microscopy investigation of lithium disilicate glass ceramic after various surface treatments-, ADVANCES IN APPLIED CERAMICS, cilt.113, ss.301-306, 2014