Mechanical properties of zirconia after different surface treatments and repeated firings

Thumbnail
View/Open
66-10.4047-jap.2014.6.6.462.pdf (785.1Kb)
Date
2014-12-01
Author
Subasi, Meryem Gulce
Demir, Necla
Kara, Ozlem
Ozturk, A. Nilgun
Ozel, Faruk
Advisor
Type
Article
Metadata
Show full item record
Abstract
This study investigated the influence of surface conditioning procedures and repeated firings on monoclinic content and strength of zirconia before cementation. MATERIALS AND METHODS. Sintered barshaped zirconia specimens were subjected to no surface treatment (control), air abrasion, or grinding (n=21). Their roughness was evaluated using a profilometer, and microscope analysis was performed on one specimen of each group. Then, 2 or 10 repeated firings (n=10) were executed, the monoclinic content of specimens was analyzed by X-ray diffraction, and a three-point flexural strength test was performed. Surface roughness values were compared using one-way analysis of variance (ANOVA) and Tukey honestly significant difference (HSD) tests, the monoclinic content values were tested using Kruskal-Wallis and Mann-Whitney U tests, and the flexural strength values were tested using two-way ANOVA and Tukey HSD tests (P=.05). Spearman’s correlation test was performed to define relationships among measured parameters. RESULTS. Surface-treated specimens were rougher than untreated specimens and had a higher monoclinic content (P<.005), and the relationship between roughness and monoclinic content was significant (P<.000). Neither surface treatment nor firing significantly affected the flexural strength, but Weibull analysis showed that for the air-abraded samples the characteristic strength was significantly lower after the 10th firing than after the 2nd firing. CONCLUSION. After firing, a negligible amount of monoclinic content remained on the zirconia surfaces, and rougher surfaces had higher monoclinic contents than untreated surfaces. Multiple firings could be performed if necessary, but the fracture probability could increase after multiple firings for rougher surfaces
Subject
Subasi M. G. , Demir N., Kara O., Ozturk A. N. , Ozel F., -Mechanical properties of zirconia after different surface treatments and repeated firings-, JOURNAL OF ADVANCED PROSTHODONTICS, cilt.6, ss.462-467, 2014
URI
https://hdl.handle.net/20.500.12645/9749
Collections
  • Diş Hekimliği Fakültesi
  • PubMed İndeksli Yayın Koleksiyonu
  • Scopus İndeksli Yayınlar Koleksiyonu
  • WoS İndeksli Yayınlar Koleksiyonu
  • Yayınlar - Eserler

BEZMIALEM VAKIF UNIVERSITY

About us |Policies | Library | Contact us | Send Feedback | Sitemap | Admin

Bezmialem Vakıf Üniversitesi, Adnan Menderes Bulvarı Vatan Caddesi 34093 Fatih, İstanbul / TURKEY
Copyright © Bezmialem Vakıf Üniversitesi

Creative Commons Lisansı
Bezmialem Institutional Repository, Creative Commons Alıntı-GayriTicari-Türetilemez 4.0 Uluslararası Lisansı ile lisanslanmıştır.

OpenAccess@BVU

Support by  UNIREPOS






sherpa/romeo

Browse

All of DSpaceCommunities & CollectionsBy Issue DateAuthorsTitlesSubjectsTypeLanguageRightsAdvisorInstitution AuthorThis CollectionBy Issue DateAuthorsTitlesSubjectsTypeLanguageRightsAdvisorInstitution Author

My Account

LoginRegister

BEZMIALEM VAKIF UNIVERSITY

About us |Policies | Library | Contact us | Send Feedback | Sitemap | Admin

Bezmialem Vakıf Üniversitesi, Adnan Menderes Bulvarı Vatan Caddesi 34093 Fatih, İstanbul / TURKEY
Copyright © Bezmialem Vakıf Üniversitesi

Creative Commons Lisansı
Bezmialem Institutional Repository, Creative Commons Alıntı-GayriTicari-Türetilemez 4.0 Uluslararası Lisansı ile lisanslanmıştır.

OpenAccess@BVU

Support by  UNIREPOS